DOW™ HDPE NG6997
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GWgGuu_DOW-HDPE-NG6997.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW™ HDPE NG6997 is a High Density Polyethylene Resin material. It is available in Latin America. Important attributes of DOW™ HDPE NG6997 are:
Typical application of DOW™ HDPE NG6997: Food Contact Applications |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.944 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 11 | g/10 min | |
| 190°C/5.0 kg | 0.38 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 380 | µm | |
| Film Puncture Resistance (380 µm) | 4.96 | J/cm³ | Internal Method |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 380 µm | 31.0 | MPa | |
| TD : Yield, 380 µm | 28.0 | MPa | |
| MD : Break, 380 µm | 49.9 | MPa | |
| TD : Break, 380 µm | 33.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 380 µm | 260 | % | |
| TD : Break, 380 µm | 530 | % | |
| Dart Drop Impact (380 µm) | 55 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 380 µm | 5.0 | g | |
| TD : 380 µm | 50 | g |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 211 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Franprene TVA 9155 | Franplast S.r.l. | SEBS | Franprene |
| FRAGOM PR/55 PP | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| Elastron® G G501.A60.B.PS | Elastron USA, Inc. | SEBS | Elastron® G |
| LEXAN™ HPH4504H resin | SABIC Innovative Plastics | PPC | LEXAN™ |
| TABOREN® PC 62 T 50 | SILON s.r.o. | PP Copolymer | TABOREN® |