Order Products : sales@su-jiao.com
Reny® 2502AH
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GVZKbd_Reny-2502AH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Reny® 2502AH is a Polyarylamide (PARA) material filled with 20% glass\mineral. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Reny® 2502AH are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.66 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 22 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 14.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.49 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.18 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.90 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 18400 | 14900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 150 | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.2 | 1.3 | % | ISO 527-2 |
| Flexural Modulus | 16500 | 14700 | MPa | ISO 178 |
| Flexural Stress | 249 | 209 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.1 | 4.3 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 27 | 29 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 235 | 229 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 217 | 206 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 3.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 5.0E+15 | 2.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 2.0E+16 | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | |||
| 1.00 mm | 27 | 26 | kV/mm | |
| 2.00 mm | 21 | 20 | kV/mm | |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | -- | 5.00 | ||
| 1 MHz | -- | 5.00 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | -- | 0.050 | ||
| 1 MHz | -- | 0.017 | ||
| Comparative Tracking Index | 200 | 300 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 275 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 120 to 145 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LAF471 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Sindustris PP HI5205S | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Arnitel® XG5857 | DSM Engineering Plastics | TPC-ET | Arnitel® |
| FHR Polypropylene P4G4B-125A | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Globalene® ST612 | Lee Chang Yung Chemical Industry Corp. | PP, Unspecified | Globalene® |