XANTAR® LDS 3732
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | XANTAR® LDS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GUzocU_XANTAR-LDS-3732.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flame Retardant (Halogen free), Laser Direct Structuring (LDS)*, Grey color only *The compound is intended specifically for the use in the process of manufacturing conducting path designs according to the German application of the patent 101 32 092 of LPKF Laser & Electronics AG. Please address straight to LPKF Laser & Electronics AG (www.LPKF.de). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 47.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C | 30 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | |||
| 23°C 1 | 20.0 | J | Internal Method |
| 23°C | 40.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 122 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 144 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 6.0E-5 | cm/cm/°C | |
| Transverse | 6.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity (1.00 GHz) | 3.30 | IEC 60250 | |
| Dissipation Factor (1.00 GHz) | 6.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | V-1 | ||
| 0.500 mm | HB |
| Note Message | |
|---|---|
| 1 . | Part with rib, Based on ISO 6603-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WONDERLOY® PC-540 | CHI MEI CORPORATION | PC+ABS | WONDERLOY® |
| Celcon® LM90Z | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Kepital® FM2020 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Karina GREEN PVC COMPOUND 602D40/365-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Evoprene™ GC 093 | Mexichem Specialty Compounds Inc. | TPE | Evoprene™ GC |