NYCOA Polyamide 1976
| Category: | Nylon 6 Alloy , Polyamide 6 Alloy |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GUxxw5_NYCOA-Polyamide-1976.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 1976 is a high viscosity resin particularly suitable for extrusion processing. NYCOA 1976 was specifically formulated to offer very high flexibility, strength, and impact toughness in extruded products. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.80 | % | ASTM D955 |
| Transverse flow | 1.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.0 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 45 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 28.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 600 | % | ASTM D638 |
| Flexural Modulus 3 | 89.6 | MPa | ASTM D790 |
| Flexural Strength 4 | 11.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | No fracture 850 J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 205 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789.Tensile Elongation at Break, ASTM D638, 2 in/min: 600+% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 216 - 227 | °C | |
| Middle Temperature | 221 - 238 | °C | |
| Front Temperature | 232 - 249 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 243 - 254 | °C | |
| Mold Temperature | 21.1 - 48.9 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 18.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® GS7033 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| TUFLIN™ HS-7001 NT 7 | The Dow Chemical Company | LLDPE | TUFLIN™ |
| DuPont™ 20 Series DPE-20-6064 | DuPont Packaging & Industrial Polymers | LDPE | DuPont™ 20 Series |
| KARIPRENE BLACK -E 6048/ 1-TRE | Karina Ind. e Com. de Plásticos Ltda | TPE | KARIPRENE |
| Diakon® Frost 952 60 | Lucite International Holland BV | Acrylic (PMMA) | Diakon® |