Ecotan A FL NERO
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Ecotan A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GUti2h_Ecotan-A-FL-NERO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66 colour black for general purpose. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 1.5 - 1.9 | % | ISO 294-4 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 8.0 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 70.0 | MPa | ASTM D638 |
| Flexural Modulus | 2600 | MPa | ASTM D790 |
| Flexural Strength (Break) | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 230 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 19 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with ISO 2577.Limit Temperature, IEC 216, 20000 hrs: 60°CTensile Elongation at Break, ASTM D638: gen-00% |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT REGRIND PC LS1-100RG | NEXT Specialty Resins, Inc. | PC | NEXT REGRIND |
| Generic PS (HIPS) | Generic | PS (HIPS) | Generic |
| Lionpol HC-204552 | Lion Polymers Incorporated | TPE | Lionpol |
| Softell TKG 317N C12740 | LyondellBasell Industries | PP Copolymer | Softell |
| 3M™ Dyneon™ PTFE Compound TF 3406 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |