INNOPOL® PP CS 2-3522 TO BU
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GUMzBC_INNOPOL-PP-CS-2-3522-TO-BU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL® CS 2-3522 TO BU is a 20% talc-filled, elastomer modified, UV-stabilized compound based on polypropylene block-copolymer. INNOPOL® CS 2-3522 TO BU is developed for producing injection moulded automotive components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 25 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 16.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.7 | % | ISO 527-2 |
| Flexural Modulus 1 | 1450 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 16 | kJ/m² | ISO 179/1eA |
| 23°C | 60 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 108 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 123 | °C | ISO 306/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 250 | °C | |
| Middle Temperature | 190 - 250 | °C | |
| Front Temperature | 190 - 250 | °C | |
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold pressure: 30 to 100 % of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cri-Line LS-918 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Fibremod™ GE277AI | Borealis AG | TPO | Fibremod™ |
| EMERGE™ PC/ABS 7700 | Trinseo | PC+ABS | EMERGE™ |
| Kepamid® 1300CRK | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| Karina CLEAR PVC COMPOUND 80/315-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |