Next Nylon 66 Industrial Series PG15-02BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Industrial Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GU8bXy_Next-Nylon-66-Industrial-Series-PG15-02BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 Glass Fiber Reinforced Black Compound Product Applications This grade is ideal used for power tools outer housing, carrying parts in automotive industries and Kitchen appliances etc Benefits Good combination Between Mechanical and thermal properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.24 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.60 | -- | % | ASTM D955 |
| Transverse flow | 1.1 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 1.8 | -- | % | ASTM D570 |
| Saturation 1 | 7.2 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| Class m | 100 | -- | ASTM D785 | |
| Class r | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5100 | 3200 | MPa | ASTM D638 |
| Tensile Strength | 120 | 85.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | 7.0 | % | ASTM D638 |
| Flexural Modulus | 4600 | -- | MPa | ASTM D790 |
| Flexural Strength | 185 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | 98 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 258 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 246 | -- | °C | ASTM D648 |
| Melting Temperature | 262 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 24 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 270 - 280 | °C | |
| Front Temperature | 270 - 280 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XANTAR® FC 22 UR | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Braskem PP TI4040WT | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| DynaMix™ XP-5529 | Polymer Dynamix | TP, Unspecified | DynaMix™ |
| Kynar® 761 | Arkema | PVDF | Kynar® |
| Lumid® GP2130B(W) | LG Chem Ltd. | Nylon 66 | Lumid® |