TOTAL Polypropylene PPR 3221
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GTrava_TOTAL-Polypropylene-PPR-3221.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene PPR 3221 is a high clarity, high impact resistance random copolymer especially designed for blow molding applications (mono and multi-layers) for food and non-food packaging of sauces, detergents and soaps, cosmetics and for sheets extrusion. Total Petrochemicals PPR 3221 is a random copolymer polypropylene with a Melt Flow Index of 1.8 g/min for the manufacturing of films with outstanding optical properties and easy heat weldability in the blown process. Polypropylene PPR 3221 is intended for food or textile packaging, for lamination films, for protection films as well as for label films. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.902 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.8 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 82 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strain (Yield) | < 15 | % | ISO 527-2 |
| Flexural Modulus | 900 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress - MD | ISO 527-3 | ||
| Yield, 40 µm, Blown Film | 35.0 | MPa | |
| Break, 40 µm, Blown Film | 70.0 | MPa | |
| Tensile Elongation - MD (Break, 40 µm, Blown Film) | 500 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 35 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 40.0 µm | 3.0 | kN/m | |
| TD : 40.0 µm | 20.0 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| 0°C | 3.6 | kJ/m² | |
| 23°C | 22 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 130 | °C | ISO 306/A50 |
| -- | 67.0 | °C | ISO 306/B50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (40.0 µm, Blown Film) | 79 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 2.1 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 225 A | RTP Company | Nylon 6 | RTP |
| Spartech Polycom EP7240 | Spartech Polycom | PP Copolymer | Spartech |
| Hostalen PP H4122 103220 | LyondellBasell Industries | PP Copolymer | Hostalen PP |
| TOTAL Polyethylene Lumicene® M 3421 UV | TOTAL Refining & Chemicals | mMDPE | TOTAL Polyethylene |
| Iupilon® MB9000 | Mitsubishi Engineering-Plastics Corp | PC+ABS | Iupilon® |