Promyde B30 P2 G30 U0. Injection Moulding Polyamide 6 with 30% glass fibre, and flame retardant using a halogen and red phosphorous free flame retardant system.

CHARACTERISTICS
Promyde B30 P2 G30 U0 is a polyamide 6 with 30% glass fibre with high mechanical strength, heat stabilized and lubricated for injection moulding. Its halogens and red-phosphorous free flame retardant system enhances its flame behavior to V0- UL rated category.

APPLICATIONS
Promyde B30 P2 G30 U0 allows a fast and efficient mould filling, and an easy mould release, that combined with its excellent mechanical properties, and its flame retardant properties make it suitable for components specially used in electrical and electronics industries.
General Information
Filler / Reinforcement
  • Glass fiber reinforced material, 30% filler by weight
Additive
  • heat stabilizer
  • Lubricant
  • Flame retardancy
Features
  • High strength
  • Fast molding cycle
  • Good formability
  • Phosphorus content, low (to none)
  • Thermal Stability
  • Lubrication
  • Good demoulding performance
  • Halogen-free
  • Flame retardancy
Uses
  • Electrical/Electronic Applications
  • Electrical components
Processing Method
  • Injection molding
PhysicalDryConditionedUnitTest Method
Density (23°C)1.40--g/cm³ISO 1183
Molding Shrinkage
     Vertical flow direction 0.70 - 0.90--%
     Flow direction 0.20 - 0.50--%
Water Absorption ISO 62
     Saturated, 23°C 6.5--%ISO 62
     Equilibrium, 23°C, 50% RH 2.1--%ISO 62
Viscosity Number 1(H2SO4 (Sulphuric Acid))125--cm³/gISO 960
MechanicalDryConditionedUnitTest Method
Tensile Modulus (23°C)99006500MPaISO 527-2/1
Tensile Stress (23°C)160110MPaISO 527-2/50
Tensile Strain (Break, 23°C)3.36.0%ISO 527-2/50
Flexural Modulus 2(23°C)93005800MPaISO 178
Flexural Stress 3(23°C)140180MPaISO 178
ImpactDryConditionedUnitTest Method
Charpy Notched Impact Strength (23°C)6.520kJ/m²ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)7095kJ/m²ISO 179/1eU
ThermalDryConditionedUnitTest Method
Heat Deflection Temperature (1.8 MPa, Unannealed)211--°CISO 75-2/A
Melting Temperature (DSC) 4220--°CISO 3146
Linear thermal expansion coefficient ISO 11359-2
     Flow : 23 to 80°C 2.0E-5--cm/cm/°CISO 11359-2
     Lateral : 23 to 80°C 6.0E-5--cm/cm/°CISO 11359-2
ElectricalDryConditionedUnitTest Method
Surface Resistivity 1.0E+131.0E+10ohmsIEC 60093
Volume Resistivity 1.0E+151.0E+12ohms·cmIEC 60093
Dielectric Constant (1 MHz)3.706.80IEC 60250
Dissipation Factor (1 MHz)0.0230.22IEC 60250
Comparative Tracking Index 600--VIEC 60112
FlammabilityDryConditionedUnitTest Method
Flame Rating UL 94
     0.800 mm V-0--UL 94
     1.50 mm V-0--UL 94
     3.00 mm V-0--UL 94
Glow Wire Flammability Index (1.50 mm)960--°CIEC 60695-2-12
Glow Wire Ignition Temperature (1.50 mm)775--°CIEC 60695-2-13
InjectionDryUnit
Drying Temperature < 80.0°C
Drying Time 4.0 - 6.0hr
Processing (Melt) Temp 250 - 270°C
Mold Temperature 40.0 - 80.0°C
Injection Rate Moderate-Fast
Injection instructions
Back pressure: moderate
Note Message
1 .0,005 g/ml H2SO4
2 .2.0 mm/min
3 .2.0 mm/min
4 .10°C/min
Resin Grade Manufacturer Category Trademark
Weatherflex™ CS1522WX NTL01B Colorite Polymers PVC, Flexible Weatherflex™
Bergamid™ B70 MI40 NC004 PolyOne Corporation Nylon 6 Bergamid™
Chemraz 655 Greene, Tweed & Co. Perfluoroelastomer Chemraz
COPYLENE® CM120LN-01 Phillips 66 PP Impact Copolymer COPYLENE®
EVAL™ E171 Kuraray Co., Ltd. EVOH EVAL™