IROGRAN® A 92 E 4670
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GSrNO5_IROGRAN-A-92-E-4670.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 92 E 4670 is a thermoplastic polyester polyurethane for melt calendering. IROGRAN is part of the HUNTSMAN technical extrusion/injection molding product range and offers a specially designed, flexible material with a broad processing window. PERFORMANCE FEATURES
APPLICATION
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | |||
| -- | 1.21 | g/cm³ | ASTM D792 |
| -- | 1.20 | g/cm³ | DIN 53479 |
| Melt Volume-Flow Rate (MVR) (190°C/10.0 kg) | 60.0 | cm³/10min | |
| Molding Shrinkage - Flow (Injection Molded) | 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, DIN 53505 | ||
| Shore A, Injection Molded | 90 | ||
| Shore D, Injection Molded | 38 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | 20 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| TMA 3 | Internal Method | ||
| High | 170 | °C | |
| Low | 125 | °C |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 4 | |||
| 100% Strain, 0.635 mm | 4.69 | MPa | ASTM D412 |
| 100% Strain, 0.635 mm | 8.50 | MPa | DIN 53504 |
| 300% Strain, 0.635 mm | 10.3 | MPa | ASTM D412 |
| 300% Strain, 0.635 mm | 16.0 | MPa | DIN 53504 |
| Tensile Strength 5 | |||
| Break, 0.635 mm | 37.9 | MPa | ASTM D412 |
| Break, 0.635 mm | 36.0 | MPa | DIN 53504 |
| Tensile Elongation 6 | |||
| Break, 0.635 mm | 570 | % | ASTM D412 |
| Break, 0.635 mm | 600 | % | DIN 53504 |
| Tear Strength 7 | |||
| 0.635 mm | 80.6 | kN/m | ASTM D624 |
| 0.635 mm | 83 | kN/m | DIN 53515 |
| Compression Set 8 | |||
| 23°C, 24 hr | 25 | % | ASTM D395, DIN 53517 |
| 70°C, 24 hr | 40 | % | ASTM D395 |
| 70°C, 24 hr | 0.40 | % | DIN 53517 |
| Bayshore Resilience | 1 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 170 | °C | |
| Cylinder Zone 1 Temp. | 175 | °C | |
| Cylinder Zone 2 Temp. | 175 | °C | |
| Cylinder Zone 3 Temp. | 175 | °C | |
| Cylinder Zone 4 Temp. | 175 | °C | |
| Cylinder Zone 5 Temp. | 175 | °C | |
| Adapter Temperature | 180 | °C | |
| Die Temperature | 180 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Injection Molded |
| 4 . | Extruded Film |
| 5 . | Extruded Film |
| 6 . | Extruded Film |
| 7 . | Extruded Film |
| 8 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID A 280 MB3 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| Dynaglide® DW 631 | DeWAL Industries | PTFE | Dynaglide® |
| Hostacom PPR 4170L | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Sylvin 7833-85 White 1348 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ OQ1028 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |