Order Products : sales@su-jiao.com
AKROMID® B3 S1 black (3726)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GSdKP6_AKROMID-B3-S1-black-3726-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 S1 black (3726) is an unreinforced, cold impact strength polyamide 6 Applications are mountings and dowels in the furniture and construction industry |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.07 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 60.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.9 | -- | % | |
| Flow | 1.5 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.0 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 7.5 | -- | % | ISO 178 |
| Tensile Modulus | 2000 | 550 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 50.0 | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 4.5 | 30 | % | |
| Break | > 50 | > 100 | % | |
| Flexural Modulus 2 | 1500 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 65.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 55 | 40 | kJ/m² | |
| 23°C | 45 | 110 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 48.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 222 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Terraloy™ BP-20001A | Teknor Apex Company | TPS+Copolyester | Terraloy™ |
| WELLAMID Nylon 6000/58 GV 15 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Adiprene® LF 1860A | Chemtura | PUR-Ester/TDI | Adiprene® |
| Polyrocks 1001T | Polyrocks Chemical Co., Ltd | PC | Polyrocks |
| Hifax TYC 852X GREY | LyondellBasell Industries | TPO (POE) | Hifax |