Wanthane® WHT-1172IC
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Wanhua Chemical Group Co., Ltd. |
| Trademark: | Wanthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GSc3xY_WanthaneWHT1172IC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TYPE: Polyester-based grade Injection molding grade FEATURES: Excellent mechanical properties, high abrasion resistance, good wear resistance, short cycle times Applications: Rigid / flexible composite systems, engineering components, etc |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| DIN Abrasion | 42.0 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 28.0 | MPa | ASTM D412 |
| Tensile Strength (Break) | 48.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 290 | % | ASTM D412 |
| Tear Strength | 260 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 24 hr | 40 | % | ASTM D395 |
| 70°C, 22 hr | 76 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -9.00 | °C | ASTM D3418 |
| Vicat Softening Temperature | 190 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 210 | °C | |
| Middle Temperature | 215 | °C | |
| Front Temperature | 220 | °C | |
| Nozzle Temperature | 225 | °C | |
| Mold Temperature | 23 | °C | |
| Screw L/D Ratio | 25.0:1.0 to 30.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stanyl® ForTii™ TX1 | DSM Engineering Plastics | Nylon 4T | Stanyl® ForTii™ |
| Iupilon® MB2112N | Mitsubishi Engineering-Plastics Corp | PC+Polyester | Iupilon® |
| LUVOCOM® 1105-7460/BL5019 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| PLANAC BT-2200 | TOYOBO America, Inc. | PBT | PLANAC |
| ESTOPLAST XU 6230NN01 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |