Polifil® PP GFPPCC-10
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | The Plastics Group |
| Trademark: | Polifil® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GSbx4L_Polifil-PP-GFPPCC-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polifil® GFPPCC series compounds are homopolymer polypropylenes reinforced with chemically coupled glass fibers. These compounds offer superior strength and stiffness, improved elevated temperature performance, better creep resistance, higher impact strength, and higher resistance to high temperature water than conventional glass fiber reinforced polypropylenes. These compounds are used in chemical resistance applications, appliances, electrical components, automotive, irrigation and utility products. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.978 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 to 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2280 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 53.8 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 3.0 | % | |
| Break, 23°C | 6.0 | % | |
| Flexural Modulus - Tangent (23°C) | 2690 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 65.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Gardner Impact (23°C, 12.7 mm) | 0.904 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 141 | °C | |
| 1.8 MPa, Unannealed | 124 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 104 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Rear Temperature | 210 to 221 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Nozzle Temperature | 227 to 249 | °C | |
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 48.9 to 65.6 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 to 0.517 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS PBT-20GFR | Polymer Technology and Services, LLC | PBT | PTS |
| TOTAL Polypropylene PPR Z9421 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| 3M™ Dyneon™ Fluoroplastic ET 6235Z | 3M Advanced Materials Division | ETFE | 3M™ Dyneon™ Fluoroplastic |
| Catalyst CT/2-LR | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| Lupox® GP1000W | LG Chem Ltd. | PBT | Lupox® |