RheTech Polyethylene E204-00
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | RheTech, Inc. |
| Trademark: | RheTech Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GSLTeh_RheTech-Polyethylene-E204-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Density Polyethylene, Natural. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.953 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 58 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 22.8 | MPa | ASTM D638 |
| Flexural Modulus | 896 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 43 | J/m | ASTM D256 |
| Dart Drop Impact | 22.6 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 65.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 44.4 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 37.8 - 48.9 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 149 - 160 | °C | |
| Middle Temperature | 154 - 171 | °C | |
| Front Temperature | 160 - 179 | °C | |
| Nozzle Temperature | 160 - 171 | °C | |
| Mold Temperature | 15.6 - 26.7 | °C | |
| Injection Pressure | 2.76 - 10.3 | MPa | |
| Holding Pressure | 2.07 - 8.27 | MPa | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Injection instructions |
|---|
| Injection Speed: Variable - Application DependantScrew RPM: Recovery 3 seconds before mold opensCycle Time: Wall Thickness Dependant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XANTAR® FC 19 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| 3M™ Dyneon™ Fluoroplastic PFA 8502ESDZ | 3M Advanced Materials Division | PFA | 3M™ Dyneon™ Fluoroplastic |
| Elastron® V V101.A79.B | Elastron USA, Inc. | TPV | Elastron® V |
| Karina BLUE COLOR CONCENTRATE 06/183-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| HiFill® HiFill® 1-10815 | Techmer Engineered Solutions | Nylon 66 | HiFill® |