HAIPLEN EP50 T2 X2
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GSHxO6_HAIPLEN-EP50-T2-X2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene copolymer talcum filled 10% self extinguishing V2, good flow and mechanical properties. Available: all colors, UV stabilized (L), heat stabilized (H), laser printable (LP), detergent stabilized(D) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.20 mm | 1.1 | % | |
| Across Flow : 3.20 mm | 1.1 | % | |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 30.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 30 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 1700 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180, ASTM D256 | ||
| -40°C | 22 | J/m | |
| -23°C | 30 | J/m | |
| 23°C | 80 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 125 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 125 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 65.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ASTM D1525, ISO 306/A 2 1 |
| -- | 80.0 | °C | ASTM D1525, ISO 306/B 3 2 |
| Ball Pressure Test (125°C) | Pass | VDE 0470 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Needle Flame Test | VDE 0471/2 | ||
| 1.60 mm | Pass | ||
| 3.20 mm | Pass |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 26 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 34S5070 | The Matrixx Group, Inc. | PBT | Matrixx |
| Microthene® MP655962 | LyondellBasell Industries | HDPE | Microthene® |
| TOTAL Polyethylene HDPE HL 428 | TOTAL Refining & Chemicals | HDPE, MMW | TOTAL Polyethylene |
| APEX® 65011 | Teknor Apex Company | PVC, Flexible | APEX® |
| Hifax X M2 U16 | LyondellBasell Industries | PP Homopolymer | Hifax |