Kepital® F25-03H
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GS6Nk5_Kepital-F25-03H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A medium-low viscosity grade for general injection molding with high-stiffness. It has improved on thermal stability. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 13 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.00 mm | 2.0 | % | ASTM D955 |
| 3.00 mm | 2.0 | % | |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 65.0 | MPa | ASTM D638 |
| Yield, 23°C | 68.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 55 | % | ASTM D638 |
| Nominal Tensile Strain at Break | 32 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2790 | MPa | ASTM D790 |
| 23°C | 2800 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 93.0 | MPa | ASTM D790 |
| 23°C | 94.0 | MPa | ISO 178 |
| Shear Strength (2.00 mm) | 56.0 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (3.20 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 158 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 112 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 101 | °C | ISO 75-2/A |
| Melting Temperature | 165 | °C | DSC |
| CLTE - Flow (20 to 80°C) | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 19 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 7.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EPQ30R | Shazand (Arak) Petrochemical Corporation | PP Copolymer | Moplen |
| NYCOA Polyamide 5015 FR | Nycoa (Nylon Corporation of America) | Nylon 66 | NYCOA Polyamide |
| KumhoSunny PBT/ASA HBA5820G | Shanghai KumhoSunny Plastics Co., Ltd. | PBT+ASA | KumhoSunny PBT/ASA |
| MAJORIS HG264 - 1298 | AD majoris | PP, Unspecified | MAJORIS |
| TECHNYL® C 218 V30 BLACK 21N | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |