LNP™ LUBRICOMP™ Noryl_NF1520 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GRz2pH_LNPLUBRICOMPNorylNF1520compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP NORYL_NF1520 compound is a 20% glass reinforced, 15% PTFE. Wear resistant; 211F HDT @ 264 psi. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.15 - 0.25 | % | Internal method |
| Transverse flow : 3.20mm | 0.25 - 0.45 | % | Internal method |
| K (wear) Factor 1 | 73.0 | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 74.5 | MPa | ASTM D638 |
| Fracture | 74.5 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 4.2 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 5310 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 101 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-dynamic | 0.46 | ASTM D1894 | |
| With steel-static | 0.30 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 360 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 16.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 103 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 6.40mm | 105 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 96.7 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 99.4 | °C | ASTM D648 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 243 - 293 | °C | |
| Middle Temperature | 254 - 299 | °C | |
| Front Temperature | 266 - 304 | °C | |
| Nozzle Temperature | 277 - 304 | °C | |
| Processing (Melt) Temp | 277 - 304 | °C | |
| Mold Temperature | 71.1 - 98.9 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.038 - 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | xE-10, PV=2000 psi-fpm vs Steel |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1490 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| THERMOLAST® K TC3SCE (Series: SCR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Wondel® B BH0 | Nanjing Julong Engineering Plastics Co., LTD | Nylon 6 | Wondel® B |
| Ultramid® A3WG10 BK00564 | BASF Corporation | Nylon 66 | Ultramid® |
| LUVOCOM® 1-0865 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |