Ultramid® A3Z3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GRnhHA_Ultramid-A3Z3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection moulding grade, mean to high impact for technical parts such as cable ducts with injection moulded special hinges, wall plugs, fasteners and clips. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.10 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.5 to 7.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2000 | 1200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 55.0 | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 10 | 20 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | > 50 | > 50 | % | ISO 527-2/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 25 | -- | kJ/m² | |
| 23°C | 60 | 80 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 170 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.10 | 5.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.10 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | -- | 600 | V | IEC 60112 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Passed | -- | FMVSS 302 | |
| Polymer Abbreviation | PA66-I | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-941U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Sylvin 2948-90 White 1516 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ESTADIENE 1218 V0/B | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| Petrotene® PP A3 C40 PRTA010 PH386 MSP | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| Riblene® FF 33 | Versalis S.p.A. | LDPE | Riblene® |