Urochem 161
| Category: | Urea Formald , Urea Formaldehyde |
| Manufacturer: | Chemiplastica, Inc. |
| Trademark: | Urochem |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GRmGpv_Urochem-161.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Urea- formaldehyde resins fortified with highly refined cellulose as filler, and further modified with minor amounts of special purpose additives, pigments, cure regulators and lubricants. The Urochem 161 Moulding Compounds can be supplied in an almost unlimited range of colours from translucent light pastels to black. Moulded parts are free from odour; UV stable with good moisture resistance. Hard, glossy and scratch resistant surface. Excellent chemical resistance. Fats, oils and common organic solvents like alcohol and acetone do not attack moulded parts which are also resistant to surfactants and weak bases. They will withstand attack from weak acids for a shorter duration. Excellent electrical properties (arc quenching, tracking, flame resistance). Oxygen index of 30% is achieved without the use of external flame retardants. No halogens are present in the composition. Compliant with the requirements of widely used material specifications for amino compounds: BS 1322 type UF A10 (*) DIN 7708 type 131.5 (*) ISO 2112 type UF A10 (*) UL certified (*) included in ISO 14527 Fields of application: The Urochem 161 Urea Moulding Compound has low shrinkage, low water absorption and high strength. It is particularly suitable for circuit breakers and electrical accessories. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | ||
| -- 1 | 0.70 to 1.0 | % | |
| -- | 0.60 to 0.80 | % | |
| Water Absorption | < 200.0 | mg | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | > 45.0 | MPa | ISO 527-2 |
| Flexural Stress | > 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | > 1.1 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | > 5.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (8.0 MPa, Unannealed) | > 90.0 | °C | ISO 75-2/C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | > 1.1E+11 | ohms·cm | IEC 60093 |
| Dielectric Constant | 5.00 | DIN 53483 | |
| Dissipation Factor (1 kHz) | < 0.10 | IEC 60250 | |
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Glow Wire Flammability Index 2 | 960 | °C | IEC 707 |
| Oxygen Index | > 30 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | Post-shrink |
| 2 . | 180 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zelux® CN-P | Westlake Plastics Company | PC | Zelux® |
| ANYPOL CL-3000F | SH Energy & Chemical | PS (EPS) | ANYPOL |
| Fainplast PVC GK 90 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Karina WHITE PVC COMPOUND -E 898-10/161-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® AC-81/SI/2 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |