UPES® 315-F
| Category: | PS+PE , Polystyrene + PE |
| Manufacturer: | NOVA Chemicals |
| Trademark: | UPES® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GReb5s_UPES-315-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UPES® 315-F is a Polystyrene + PE (PS+PE) material. It is available in North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.980 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.14 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2060 | MPa | ASTM D638 |
| Tensile Strength 1(Break) | 33.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.7 | % | ASTM D638 |
| Flexural Modulus | 1910 | MPa | ASTM D790 |
| Flexural Strength 3(Yield) | 58.0 | MPa | ASTM D790 |
| Flexural Strain - Yield 4 | > 5.0 | % | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 26 | J/m | ASTM D256 |
| Unnotched Izod Impact | 880 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 105 | °C | ASTM D1525 5 |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 5.1 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | Testing speed of .05 inches/minute |
| 5 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene 815 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| TOYOBO Urethane E2080A | TOYOBO America, Inc. | PUR-Capro | TOYOBO Urethane |
| Ferro PP TPP40AN65BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Hifax TYL 250P | LyondellBasell Industries | PP, Unspecified | Hifax |
| SABIC® LLDPE 518NJ | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |