KMI PP KM-1755
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | KMI Group, Inc. |
| Trademark: | KMI PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GR2KDM_KMIPPKM1755.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KM-1755 is a impact copolymer polypropylene for injection molding. Applications: Baskets, pails, toys, and applications requiring extra toughness |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 23.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 7.0 | % | ASTM D638 |
| Flexural Modulus | 1170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 190 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 90.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 148 | °C | ASTM D1525 |
| Melting Temperature | 160 - 165 | °C | Internal method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cellophane™ 390MSC | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Formolene® 2306N | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Latene® AG7H2 G/50 | LATI S.p.A. | PP Homopolymer | Latene® |
| IROGRAN® A 78 E 4506 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| Karina BLACK PVC COMPOUND 956-48/1-C-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |