NIMA NH PA66UT
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | NIMA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GQSGf2_NIMA-NH-PA66UT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66 - Ultra Tough, Flame retarded Non-Hal grade with excellent retention of mechanical properties. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.17 mm | 1.1 to 1.3 | % | |
| Across Flow : 3.17 mm | 0.35 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1400 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 38.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 20 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 1700 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 55.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 73.0 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 58.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRISAN NF2100 | Formosa Plastics Corporation | SAN | TAIRISAN |
| COSMOTHENE® EVA H2181 | TPC, The Polyolefin Company (Singapore) Pte Ltd | EVA | COSMOTHENE® EVA |
| LEXAN™ HPS1 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Iupiace® GH20 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| Lutene® H ME8000 | LG Chem Ltd. | HDPE | Lutene® H |