Evolue™ SO2530S
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Prime Polymer Co., Ltd. |
| Trademark: | Evolue™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GQNdRD_Evolue-SO2530S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Evolue™SO2530S is a linear low density polyethylene product,. It can be processed by pipeline extrusion molding or extrusion, and is available in North America, Europe or Asia Pacific. Typical application areas are: water pipes/pipes/drinking water. The main characteristics are: good rigidity. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.6 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (Injection Molded) | > 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Injection Molded) | 56 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, Injection Molded) | 18.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 390 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (Injection Molded) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 101 | °C | ISO 306 |
| Melting Temperature (DSC) | 122 | °C | ISO 3146 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Micholac D2000 | API Polymers, Inc. | ABS | Micholac |
| Globalene® 6331-11 | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| Globalene® 6181 | Lee Chang Yung Chemical Industry Corp. | PP Random Copolymer | Globalene® |
| Karina BLACK PVC COMPOUND 851D48/ 1-A-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TECHNYL STAR® S 218 V30 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR® |