MonoSol® M6030
| Category: | PVOH , Polyvinyl Alcohol |
| Manufacturer: | MonoSol, LLC |
| Trademark: | MonoSol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GQIgGD_MonoSol-M6030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MonoSol M6030 is a PVOH based thermoplastic film, soluble in cold water and manufactured using MonoSol's proprietary solution cast technology. MonoSol M6030 is a rapidly dissolving clear PVOH film used for unit dose packaging of industrial and household cleaning compounds. Its relatively high modulus makes it particularly suitable for small pouching and tight wrapping applications. This film is commonly used for Toilet Block Disinfectants, Deodorizers and Cleaners and is converted on conventional pleat wrapping and flow-wrapping. Standard thicknesses are 20 micron (0.8 mil) and 25 micron (1.0 mil). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Solubility 1 | |||
| Disintegration : 10°C, 25.4 µm | 7.9 | sec | |
| Dissolution : 10°C, 25.4 µm | 20.0 | sec |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yield (25.4 µm) | 2.99 | m²/kg | ASTM D4321 |
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 20 µm and 25 µm | ||
| Secant Modulus - 100%, MD | 20.0 | MPa | ASTM D882, ISO 527-3 |
| Tensile Strength - MD | |||
| Break | 31.0 | MPa | ASTM D882 |
| -- | 31.0 | MPa | ISO 527-3 |
| Tensile Elongation - MD (Break) | 260 | % | ASTM D882, ISO 527-3 |
| Note Message | |
|---|---|
| 1 . | Distilled Water (MSTM 205) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 MV 14 | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Sumikon® VM 3615G | Mitsubishi Chemical Corporation | PVC, Rigid | Sumikon® VM |
| XYLEX™ X8303CL resin | SABIC Innovative Plastics Asia Pacific | PC+Polyester | XYLEX™ |
| Compoceran E102B | Arakawa Chemical Industries, Ltd. | Epoxy | Compoceran |
| FILLMA 5002G30 | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | FILLMA |