LNP™ THERMOCOMP™ RF009S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GQ5LlQ_LNP-THERMOCOMP-RF009S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RF009S is a compound based on Nylon 66 resin containing 45% Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound RF-1009 HS Product reorder name: RF009S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.54 | g/cm³ | |
| -- | 1.53 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.40 to 0.70 | % | |
| Across Flow : 24 hr | 1.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.54 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.77 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 14100 | MPa | ASTM D638 |
| -- | 14000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 211 | MPa | ASTM D638 |
| Break | 214 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.9 | % | ASTM D638 |
| Break | 2.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 13500 | MPa | ASTM D790 |
| -- 5 | 12000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 307 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 337 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D256 |
| 23°C 7 | 19 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1300 | J/m | ASTM D4812 |
| 23°C 8 | 82 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 11.9 | J | ASTM D3763 |
| -- | 4.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 261 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 259 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 254 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 247 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PP HLR102 | Sasol Polymers | PP Homopolymer | Sasol Polymers PP |
| SUPRAN® PP1340 | SAMBARK | PP, Unspecified | SUPRAN® |
| Wellamid® XT1668-BK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| KOPLA PP KPU1015 | KOPLA Co., Ltd. | PP, Unspecified | KOPLA PP |
| Plaslube® PA6/6 GF30 TL5 LE | Techmer Engineered Solutions | Nylon 66 | Plaslube® |