InnoTooling™ IE-644-05
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTooling™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GQ0Xxw_InnoTooling-IE-644-05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-644-05 is a tough, abrasion resistant urethane formulated for room temperature meter-mix dispensing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.14 | g/cm³ | |
| Base Resin | 1.14 | g/cm³ | |
| Hardener | 1.18 | g/cm³ |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 262 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 320 | J/m | ASTM D256 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 50 Mix Ratio by Weight: 51 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 10 to 20 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.080 | Pa·s | |
| 25°C 2 | 2.8 | Pa·s | |
| 25°C 3 | 5.8 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 1.3 to 1.8 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 50 to 60 | ASTM D2240 | |
| Tensile Strength | 19.3 | MPa | ASTM D638 |
| Tensile Elongation at Break | 20 | % | ASTM D638 |
| Tear Strength | 61.3 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 24 hours at 77°F + 16 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UMG ABS® EX215 | UMG ABS, Ltd. | ABS | UMG ABS® |
| Arnitel® PL381-H | DSM Engineering Plastics | TPC-ET | Arnitel® |
| Hyundai EP PA6 LS135 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| INEOS PP H00G-00 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| Cereplast Compostables® 4001 | Trellis Bioplastics | PLA | Cereplast Compostables® |