Makroblend® DP7645
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makroblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GPoPMU_Makroblend-DP7645.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| (PC+PET) blend, impact modified, Injection molding grade, unreinforced |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow 1 | 0.60 to 0.80 | % | |
| Across Flow : 90°C, 1 hr | 0.10 to 0.20 | % | |
| Flow 2 | 0.60 to 0.80 | % | |
| Flow : 90°C, 1 hr | 0.10 to 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 100 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2100 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 50.0 | MPa | |
| Break, 23°C | 40.0 | MPa | |
| Tensile Strain (Yield, 23°C) | 4.5 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 3(23°C) | 2100 | MPa | ISO 178 |
| Flexural Stress 4 | ISO 178 | ||
| 23°C | 75.0 | MPa | |
| 3.5% Strain, 23°C | 65.0 | MPa | |
| Flexural Strain at Flexural Strength 5(23°C) | 5.7 | % | ISO 178 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate - US-FMVSS (> 1.00 mm) | passed | ISO 3795 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gottfert Melt Viscosity 6(260°C) | 600 | Pa·s | Internal Method |
| ISO Shortname | ISO 7792-PC/PET,MHPR,-020 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 55 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/A | ||
| -20°C | 23 | kJ/m² | |
| -10°C | 45 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 94.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 133 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 7.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 7.0E-5 | cm/cm/°C | |
| Thermal Conductivity 7(23°C) | 0.20 | W/m/K | ISO 8302 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| Oxygen Index 8 | 20 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 600 bar |
| 2 . | 600 bar |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2 mm/min |
| 6 . | 165/s |
| 7 . | Cross-flow |
| 8 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4005 A | RTP Company | PPA | RTP |
| apilon 52® A-8505 | API SpA | TPU-Polyester | apilon 52® |
| Ghaed ABS ABS-HU-650 | Ghaed Basir Petrochemicals Co. | ABS | Ghaed ABS |
| Laticonther 87/28 GR/50 | LATI S.p.A. | PC | Laticonther |
| LNP™ THERMOCOMP™ 2F006 compound | SABIC Innovative Plastics | ETFE | LNP™ THERMOCOMP™ |