LNP™ LUBRICOMP™ IFL36R compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GPlXNG_LNP-LUBRICOMP-IFL36R-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Internally lubricated PA6.12, containing Glass Fiber and PTFE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8700 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 148 | MPa | |
| Break | 147 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 3.3 | % | |
| Break | 3.4 | % | |
| Flexural Modulus 1 | 7300 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 200 | MPa | |
| -- 4 | 198 | MPa | |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.55 | ||
| vs. Itself - Static | 0.50 | ||
| Wear Factor - Washer | 9.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 5(23°C) | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6(23°C) | 70 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7(1.8 MPa, Unannealed, 64.0 mm Span) | 197 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.8E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.0E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 304 TFE 5 | RTP Company | PC | RTP |
| Unichem 91-477 | Colorite Polymers | PVC, Unspecified | Unichem |
| Geon™ Vinyl Rigid Extrusion 87416 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Huafon JF-A-AH5055 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| LNP™ THERMOCOMP™ JF006E compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |