K-Resin® SBC KR03
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | K-Resin® SBC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GPMRkO_K-Resin-SBC-KR03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
K-Resin® SBC KR03 is a Styrene Butadiene Block Copolymer (SBC) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for compounding, extrusion, injection molding, profile extrusion, sheet extrusion, or thermoforming. Important attributes of K-Resin® SBC KR03 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 7.5 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | 0.090 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 26.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.18 mm) | 230 | % | ASTM D638 |
| Flexural Modulus 3(3.18 mm) | 1800 | MPa | ASTM D790 |
| Flexural Strength 4(3.18 mm) | 37.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact 5(23°C, 3.18 mm, Total Energy) | 40.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 62.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (60°) | 162 | ASTM D523 | |
| Transmittance | 92.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 177 to 232 | °C | |
| Mold Temperature | 10.0 to 48.9 | °C | |
| Back Pressure | 0.345 to 1.03 | MPa | |
| Clamp Tonnage | 2.8 to 8.3 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | 13 mm/min |
| 4 . | 13 mm/min |
| 5 . | 3.81 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borcoat™ ME0420 | Borealis AG | PE, Unspecified | Borcoat™ |
| INSTRUC PCPETGF10 | Infinity LTL Engineered Compounds | PC+PET | INSTRUC |
| LEXAN™ VR2920 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LNP™ THERMOCOMP™ RC006XXH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Lucent PC PC/PBT-1422 | Lucent Polymers, Inc. | PC+PBT | Lucent PC |