XYRON™ X1744
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | XYRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GP43r3_XYRON-X1744.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Modified PPE 35% Filler reinforced Flame retardant V-1 Stiffness High, Warpage Low, Easy Flow |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1(2.00 mm) | 0.15 to 0.43 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 7500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 5.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 120 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 118 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 65°C) | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.40 | ||
| 1 MHz | 3.30 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 7.0E-3 | ||
| 1 MHz | 9.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-1 | ||
| 3.00 mm | V-0 | ||
| 2.20 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 300 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 150x150x2 mm |
| 2 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-6635C | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Grilamid® XE 4158 nat | EMS-GRIVORY | Nylon 12 | Grilamid® |
| Hostacom PPU X9057HSHL23 | LyondellBasell Industries | PP Copolymer | Hostacom |
| KumhoSunny PBT/ABS HAB8740B | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+PBT | KumhoSunny PBT/ABS |
| JSR EPR EBM2011P | JSR Corporation | EPDM | JSR EPR |