Badamid® PA12 M20 FR V5
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GOsL4R_BadamidPA12M20FRV5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid®PA12 M20 FR V5 is a polyamide 12 (nylon 12) material,. This product is available in Europe, and the processing method is injection molding. Badamid®The main characteristics of PA12 M20 FR V5 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Volume-Flow Rate (MVR) (235°C/2.16 kg) | 40.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 1.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 5.5 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2(1.8 MPa, Unannealed, 4.00 mm) | 150 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 3 | 178 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.40 mm | V-0 | UL 94 | |
| 3.0 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.6 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.6 mm) | 775 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| Maximum Service Temperature, IEC 216, some hours: 140°CMaximum Service Temperature, IEC 216, 20000 hours: 110°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 40 - 60 | °C |
| Note Message | |
|---|---|
| 1 . | 80x10x4 mm |
| 2 . | 110x10x4 mm |
| 3 . | Compound for molding, 10k/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILPURAN® 6000/05 A/B | Wacker Chemie AG | Silicone | SILPURAN® |
| Viprene™ P55A-22U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| Globalene® 73F4-3 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| MAJORIS GFRH210 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| Sumiliteresin® PR-13349 IP | SBHPP | Phenolic | Sumiliteresin® |