SABIC® LDPE 2404H4
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GOSqAO_SABIC-LDPE-2404H4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2404H4 is a grade with a high level of anti block and slip agent (E=erucamide). The grade has a very good draw down ability. Typically films produced from this grade are stiff, have very good optical properties, low CoF and no blocking. Application SABIC® LDPE 2404H4 is typically used for stiffer thin films for textile packaging. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.7 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.20 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 25 µm, blown film | 240 | MPa | ISO 527-3 |
| TD : 25 µm, blown film | 250 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, blown film | 12.0 | MPa | ISO 527-3 |
| TD : Yield, 25 µm, blown film | 12.0 | MPa | ISO 527-3 |
| MD : Broken, 25 µm, blown film | 28.0 | MPa | ISO 527-3 |
| TD : Broken, 25 µm, blown film | 16.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 25 µm, blown film | 100 | % | ISO 527-3 |
| TD : Broken, 25 µm, blown film | > 500 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown Film (25.0 µm) | 130 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking - Blown Film (25.0 µm) | g | Internal method | |
| Re-blocking - Blown Film (25.0 µm) | 20 | g | Internal method |
| Tear Strength 1 | ISO 6383-2 | ||
| MD : 25.0 µm | 90.0 | kN/m | ISO 6383-2 |
| TD : 25.0 µm | 30.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 94.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 11 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film properties have been measured at film of 25 µm with a BUR of 3.The film has been produced on Kiefel IBC blown film line with 200 kg/h. Die size 200 mm, die gap 0.8 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-FR1-D-(color)-3 | Polymer Resources Ltd. | PC | PRL |
| TYRIL™ 867 E UV | Trinseo | SAN | TYRIL™ |
| Akulon® K224-PG6 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Karina WHITE PVC COMPOUND -E 839-10/158-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Thermec N™ 4314T1H | Technical Polymers, LLC | PPA | Thermec N™ |