Order Products : sales@su-jiao.com
EZ-Brush® Vacuum Bagging Silicone
| Category: | Silicone , Silicone |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | EZ-Brush® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GO6GXm_EZ-Brush-Vacuum-Bagging-Silicone.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EZ-Brush® Vac Bag Silicone is a brushable platinum cure silicone developed especially for making high performance, re-usable vacuum bags. EZ-Brush® Vac Bag Silicone is easy to mix and apply. Mix ratio is 1A:1B by volume and rubber can be applied with a brush or spatula to vertical surfaces without sagging. Pot life is 30 minutes, recoat time is 1 hour. Rubber cures with negligible shrinkage to a soft, flexible rubber (Shore 20A) with very high elongation and tear strength. Newly made bags can be removed from the tool in 3.5 hours and used immediately in production with polyester or epoxy resin systems and will withstand temperatures up to 500° F /260° C. Compared to conventional vacuum bagging systems, EZ-Brush® Vac Bag Silicone is much faster at delivering a production-ready silicone bag resulting in a tremendous time and labor savings. Since bags are re-usable, long term material costs are greatly reduced. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.928 | cm³/g | ASTM D1475 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 1A:1B by volume |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | < 0.10 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 20 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 0.317 | MPa | ASTM D412 |
| Tensile Strength (Break) | 3.79 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 360 | % | ASTM D412 |
| Tear Strength 1 | 21.0 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 30 | min | ASTM D2471 |
| Thermoset Mix Viscosity | 20000 | cP | ASTM D2393 |
| Demold Time (23°C) | 210 | min |
| Note Message | |
|---|---|
| 1 . | Die B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC/ABS-G10 | Polymer Resources Ltd. | PC+ABS | PRL |
| NEOFLON™ AP-210 | DAIKIN AMERICA, INC. | PFA | NEOFLON™ |
| Larton G/40 I6 | LATI S.p.A. | PPS | Larton |
| Idemitsu PS NS-100 | Idemitsu PS | PS (HIPS) | Idemitsu PS |
| Infino XP-2165M | SAMSUNG SDI CO., LTD. | PPS | Infino |