Capilene® W 77 AV
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Capilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GNsGdp_Capilene-W-77-AV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CAPILENE ® W 77 AV is a controlled rheology polypropylene homopolymer intended for injection molding. CAPILENE ® W 77 AV features: controlled rheology, nucleating and antistatic additives, very high flow, high stiffness, low warpage and short molding cycle time. CAPILENE ® W 77 AV is suitable for: thin walled packaging items, products with long flow length or complex design, household articles and toys. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 55 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 38.0 | MPa | ASTM D638 |
| Yield | 36.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 9.0 | % | ASTM D638 |
| Yield | 9.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 1800 | MPa | ASTM D790 |
| -- 3 | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 20 | J/m | ASTM D256 |
| 23°C | 2.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 108 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ASTM D1525 4 |
| -- | 155 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-758R | CHI MEI CORPORATION | ABS | POLYLAC® |
| Rotec® ABS 1001 FR V0/4 | ROMIRA GmbH | ABS | Rotec® ABS |
| Ultramid® B3L BK00464 | BASF Corporation | Nylon 6 | Ultramid® |
| Koattro KT AR05 | LyondellBasell Industries | Plastomer | Koattro |
| Karina WHITE PVC COMP E 880-10/136-A-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |