HIFOR® LT74104
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | HIFOR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GNKMXq_HIFOR-LT74104.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| WESTLAKE Hifor Polyethylene LT74104 is a high strength linear low density polyethylene containing no slip of antiblock. It is designed for blown applications and is well suited for consumer and industrial packaging markets which require good impact and tear strength. Films produced usign LT74104 exhibit low imperfections and facilitate production at thinner guages. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D4883 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD | 220 | MPa | |
| 1% Secant, TD | 241 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break | 50.0 | MPa | |
| TD : Break | 39.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 750 | % | |
| TD : Break | 1000 | % | |
| Dart Drop Impact | 170 | g | ASTM D1709 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 60 | ASTM D2457 | |
| Haze | 8.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Propionate 360E4861312 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| MonoSol® M8900 | MonoSol, LLC | PVOH | MonoSol® |
| UBE Polyethylene F522N | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Hy-Vin® XR80210 | INEOS Compounds | PVC, Flexible | Hy-Vin® |
| TECHNYL® B 218 MT25 V15 BLACK 21 N | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |