Durethan® BKV 215 W1 902176
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GN0vvg_Durethan-BKV-215-W1-902176.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, weather stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.18 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 280°C, 2.00 mm 1 | 0.60 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.10 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 0.50 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.10 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 4400 | 2100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 85.0 | 50.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 4.7 | 20 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 3900 | 1900 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 115 | 50.0 | MPa | |
| 23°C 6 | 135 | 65.0 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 5.5 | 7.5 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 8 | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6/66-HI, GLR, 14-040, GF15 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 80 | kJ/m² | |
| 23°C | 65 | 100 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 20 | 30 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 60 | 60 | kJ/m² | |
| 23°C | 55 | 80 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 3.10 | -- | J | |
| 23°C | 7.30 | -- | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 785 | -- | N | |
| 23°C | 1760 | -- | N |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 205 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | 193 | -- | °C | ISO 306/B120 |
| Melting Temperature 9 | 214 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 5.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.6E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | US-FMVSS302 |
| 9 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADMER™ AT2539E | Mitsui Chemicals Europe GmbH | MDPE | ADMER™ |
| Expandable PS F32MB-n | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| Eltex® P KV349 | INEOS Olefins & Polymers Europe | PP Random Copolymer | Eltex® P |
| Karina MBU BROWN E 3600/004-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LEXAN™ ML6411 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |