DURACON® M270LV
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | DURACON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GMwMN7_DURACON-M270LV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low VOC |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 27 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 23.0 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2650 | MPa | ISO 527-2 |
| Tensile Stress | 63.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 30 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | 86.0 | MPa | ISO 178 |
| Coefficient of friction- Dynamic | JIS K7218 | ||
| -- 1 | 0.370 | JIS K7218 | |
| -- 2 | 0.470 | JIS K7218 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color Number | CF2001/CD3069 | ||
| Specific Wear | JIS K7218 | ||
| -- 3 | 10^-3 mm³/N·km | JIS K7218 | |
| -- 4 | 1.50 | 10^-3 mm³/N·km | JIS K7218 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 95.0 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | Internal method | ||
| Flow : 23 to 55°C | 1.1E-4 | cm/cm/°C | Internal method |
| Lateral : 23 to 55°C | 1.1E-4 | cm/cm/°C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Pressure | 49.0 - 98.0 | MPa | |
| Screw Speed | 100 - 150 | rpm |
| Injection instructions |
|---|
| Injection Speed: 5-50mm/s (0.3-3m/min)Molding Cycle: Injection Holding Pressure: Gate sealing time + alpha Cooling: Plasticizing time or ejection capable time |
| Note Message | |
|---|---|
| 1 . | vs M90-44, pressure0.06MPa, 15cm/s |
| 2 . | vs C-Steel, pressure 0.49MPa, 30cm/s |
| 3 . | vs C-Steel, steel side, pressure 0.49MPa, 30cm/s |
| 4 . | vs C-Steel, material side, pressure 0.49MPa, 30cm/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT PCR PA66 G33-300PCR | NEXT Specialty Resins, Inc. | Nylon 66 | NEXT PCR |
| Novalloy-A A1300, A1300F | Daicel Polymer Ltd. | ABS+Nylon | Novalloy-A |
| Akulon® K225-KWS | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Cellophane™ XS340 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Delrin® 311DP BK402 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |