Techsil RTV1084G
| Category: | Silicone , Silicone |
| Manufacturer: | Techsil Limited |
| Trademark: | Techsil |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GMwLfA_Techsil-RTV1084G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
RTV1084G is a non-corrosive, 1-part, room temperature vulcanising (RTV) silicone rubber. It is one of a new family of products called acetone cure sealants. These products are cured rapidly in contact with atmospheric moisture to a tough rubber that exhibits an excellent thermal conductive property of ~2.3 W/m K. RTV1084G does not corrode copper or its alloys and exhibits excellent primerless adhesion to many substrates when fully cured. Key Features:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.11 | g/cm³ | BS 903 |
| Molding Shrinkage - Flow | 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shear Strength | ASTM D1002 | ||
| -- 1 | 2.98 | MPa | |
| -- 2 | 0.701 | MPa | |
| -- 3 | 0.353 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 4(Yield) | 3.90 | MPa | BS 903 |
| Tensile Elongation 5(Break) | 100 | % | BS 903 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE | |||
| Flow | 1.6E-4 | cm/cm/°C | |
| Transverse | 4.9E-4 | cm/cm/°C | |
| Thermal Conductivity | 2.3 | W/m/K | |
| Service Temperature 6 | -50 to 220 | °C |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Tack Free Time 7(23°C) | 4.0 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cure Time 8(23°C, 3.00 mm) | < 8.0 | hr | |
| Extrusion Rate | 390 | g/min |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | > 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.90 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 9.0E-4 | ASTM D150 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Mix Viscosity 9 | 35000 | cP |
| Note Message | |
|---|---|
| 1 . | Stainless Steel 304 |
| 2 . | Aluminum |
| 3 . | Copper |
| 4 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 5 . | after 7 days cure at 23+/-2°C and 65% relative humidity |
| 6 . | AFS 1540B |
| 7 . | 65%RH |
| 8 . | 65%RH |
| 9 . | Brookfield |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ LLDPE MP 1888.11 Copolymer | The Dow Chemical Company | LLDPE | DOW™ LLDPE |
| Beetle® PPC120M 9250 | Teknor Apex Company (Chem Polymer) | PP Copolymer | Beetle® |
| Hylox® 9015 | Ravago Manufacturing Americas, LLC | PBT | Hylox® |
| INLUBE PBTCF30TF15 | Infinity LTL Engineered Compounds | PBT | INLUBE |
| 3M™ Dyneon™ Fluoroelastomer FC 2177 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |