AVALON® 90 AKU
| Category: | TPU, Unspecified , Thermoplastic Polyurethane Elastomer |
| Manufacturer: | Huntsman Corporation |
| Trademark: | AVALON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GMgXvy_AVALON-90-AKU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AVALON 90 AKU is a UV-stabilised, high performance, thermoplastic polyurethane-based material for injection moulding. AVALON 90 AKU is part of the AVALON Crystal Range and offers a specially designed, flexible material with a higher degree of transparency compared with conventional TPU at the same hardness. AVALON Crystal materials are particularly suitable for the sporting goods and fashion markets and are supplied with a high level of stabilisation against premature yellowing from sunlight. The features offered include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 2781 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw A | 90 | ISO 868 | |
| Shaw D | 44 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ross Flex 1 | |||
| -10°C | > 5.0E+4 | Cycles | |
| 23°C | > 5.0E+4 | Cycles | |
| Abrasion Resistance | 50.0 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 100% strain | 8.00 | MPa | ISO 37 |
| 300% strain | 16.0 | MPa | ISO 37 |
| Tensile Stress (Break) | 45.0 | MPa | ISO 37 |
| Tensile Elongation (Break) | 450 | % | ISO 37 |
| Tear Strength 2 | 110 | kN/m | ISO 34-1 |
| Additional Information |
|---|
| Test plates conditioned 20 hours at 100°C before testing |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 - 90.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 | hr | |
| Hopper Temperature | 25.0 - 35.0 | °C | |
| Rear Temperature | 195 - 205 | °C | |
| Middle Temperature | 205 - 215 | °C | |
| Front Temperature | 210 - 220 | °C | |
| Nozzle Temperature | 205 - 215 | °C | |
| Mold Temperature | 25.0 - 50.0 | °C | |
| Injection Pressure | 2.00 - 10.0 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 1.00 - 5.00 | MPa | |
| Back Pressure | 0.0300 - 0.300 | MPa | |
| Screw Speed | 20 - 80 | rpm | |
| Screw L/D Ratio | 20.0:1.0 to 25.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Injection instructions |
|---|
| Typical Screw Diameter : 40 - 120 mm3 Stage Design Feed Zone : 0.4L Compression Zone : 0.3L Metering Zone : 0.3L |
| Note Message | |
|---|---|
| 1 . | BS 5131 |
| 2 . | Method B, right-angle specimen (without cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 600 A/B RED | Wacker Chemie AG | Silicone | POWERSIL® |
| Celstran® PP-GF60-25 AD3002 Black | Celanese Corporation | PP, Unspecified | Celstran® |
| HiFill® PA6 GF33 IM L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| LNP™ STAT-KON™ LX00797C compound | SABIC Innovative Plastics | PEEK | LNP™ STAT-KON™ |
| Petra® 130 | BASF Corporation | PET | Petra® |