CYCOLOY™ CX2244ME resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GLon63_CYCOLOY-CX2244ME-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CYCOLOY CX2244ME resin is a flame retardant PC/ABS blend featuring excellent balance of flow and impact together with UL-94 V0 rating at < 1mm. CYCOLOY CX2244ME resin also demonstrates improved chemical resistance to general hospital cleaners which can be considered for healthcare enclosure applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 | g/cm³ | ASTM D792 |
| -- | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.60 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.20 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2600 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 65.0 | MPa | ASTM D638 |
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Break 3 | 58.0 | MPa | ASTM D638 |
| Break | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.1 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/50 |
| Break 5 | 100 | % | ASTM D638 |
| Break | 90 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2500 | MPa | ASTM D790 |
| -- 7 | 2500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 96.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 104 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 180 | J/m | ASTM D256 |
| 23°C | 700 | J/m | ASTM D256 |
| -30°C 10 | 10 | kJ/m² | ISO 180/1A |
| 23°C 11 | 40 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 65.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 89.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 93.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 110 | °C | ASTM D1525, ISO 306/B50 11 13 |
| -- | 113 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.5E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.5E-5 | cm/cm/°C | |
| RTI Elec | 90.0 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI Str | 90.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | 5VB | ||
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (3.00 mm) | 800 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 230 to 280 | °C | |
| Middle Temperature | 240 to 290 | °C | |
| Front Temperature | 250 to 300 | °C | |
| Nozzle Temperature | 250 to 300 | °C | |
| Processing (Melt) Temp | 250 to 300 | °C | |
| Mold Temperature | 60.0 to 85.0 | °C | |
| Vent Depth | 0.030 to 0.075 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 |
| 11 . | 80*10*3 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL NY6-M25G15- (color)H | Polymer Resources Ltd. | Nylon 6 | PRL |
| WPP PP PPC3GF1.5-Black | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| DuraMax™ DMX 8080NC | Advanced Polymer Alloys | TPE | DuraMax™ |
| HiPrene® M560ST | GS Caltex | PP Impact Copolymer | HiPrene® |
| Karina GREEN PVC COMPOUND 902-40/101-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |