EL-Lene™ H555JA
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GLmkU8_EL-Lene-H555JA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Lene H555JA is a high density polyethylene resin with good environmental stress cracking resistance, good processing performance, organoleptic property. It is particularly designed for injection molding and extrusion compression molding of screw cap and closure. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.8 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 2.00 mm | 2.5 | % | |
| Across Flow : 2.00 mm | 2.3 | % | |
| Environmental Stress-Cracking Resistance (50°C, 10% Igepal, Compression Molded, F50) | 20.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 25.5 | MPa | |
| Break | 34.3 | MPa | |
| Tensile Elongation 2(Break) | 1200 | % | ASTM D638 |
| Flexural Modulus | 1080 | MPa | ASTM D790 |
| Flexural Strength | 32.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 78.0 | °C | ASTM D648 |
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Melting Temperature | 131 | °C | ASTM D2117 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 240 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 180 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAISOX 3310 | Formosa Plastics Corporation | LLDPE | TAISOX |
| Forprene® 6NM901A65 | SO.F.TER. SPA | TPV | Forprene® |
| Edgetek™ PS-30CF/000 HF UV BLACK | PolyOne Corporation | PBT | Edgetek™ |
| Horda E8413 | Horda Cable Compounds | PE, Unspecified | Horda |
| LG ASA LI912-WNPZ | LG Chem Ltd. | ASA | LG ASA |