STERLENE™ BMV213A
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | R&P (Pte.) Ltd. |
| Trademark: | STERLENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GLWqTX_STERLENE-BMV213A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| STERLENE™ BMV213A is a compound designed for automotive interior applications requiring very high impact resistance as well as high stiffness with superior scratch resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 24 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2/50 |
| Tensile Stress (Yield, 23°C) | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 4.5 | % | |
| Break, 23°C | 26 | % | |
| Flexural Modulus 2(23°C) | 2170 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 32.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -40°C, Complete Break | 4.6 | kJ/m² | |
| 23°C, Partial Break | 30 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -40°C, Complete Break | 5.4 | kJ/m² | |
| 23°C, Partial Break | 35 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 240 | °C | |
| Mold Temperature | 25.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure B |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermovin™ 170-H7 | Vi-Chem Corporation | PVC, Unspecified | Thermovin™ |
| Next ABS SG15-01BK | Next Polymers Ltd. | ABS | Next ABS |
| Gallonprene® GP420-8501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Hifax TKC 243P Black | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Petrothene® LB560201 | LyondellBasell Industries | HDPE | Petrothene® |