Starpylen M1000-BK1A987
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starpylen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GL8oKX_Starpylen-M1000-BK1A987.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starpylen M1000-BK1A987 is a high carbon black loaded PP resin. |
| General Information | |
|---|---|
| Additive |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 6.0 to 12 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.00 mm) | 1.5 to 2.0 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 2600 | MPa | ISO 178 |
| Flexural Stress | 54.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 1(23°C) | 9.0 | kJ/m² | ISO 179/1eU |
| Unnotched Izod Impact Strength 2(23°C) | 14 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 100 mm Span) | 75.0 | °C | ISO 75-2/Ae |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 220 to 230 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Processing (Melt) Temp | 220 to 230 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 120*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP2S34F | Shazand (Arak) Petrochemical Corporation | PP Random Copolymer | Moplen |
| TAROPRENE® 1 A55 E1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| TULAMID® PA-SV30-IR | UCC Shchekinoazot | Nylon 6 | TULAMID® |
| Ultramid® Aqua UV BK20592 | BASF Corporation | Nylon 66 | Ultramid® |
| Jampilen RCXP599 | Jam Polypropylene Company | PP Random Copolymer | Jampilen |