ALCOM® AWL 109/10 WT1218-11LB
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® AWL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GKstwR_ALCOM-AWL-109-10-WT1218-11LB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM® AWL 109/10 WT1218-11LB is a Polycarbonate + ABS (PC+ABS) product filled with 10% filler. It is available in Asia Pacific, Europe, or North America. Applications of ALCOM® AWL 109/10 WT1218-11LB include automotive, lighting applications and reflectors. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 24 hr | 0.10 | % | |
| Flow : 24 hr | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 115 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 50.0 | MPa | |
| Break | 39.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 3.0 | % | |
| Break | 13 | % | |
| Flexural Modulus | 2500 | MPa | ISO 178 |
| Flexural Stress | 78.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 109 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Fire Performance (2.00 mm) | passed | FMVSS |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tristimulus Value | |||
| Y10 of Reflection | 85 | % | DIN 5033 |
| Y10 of Transmittance : 500.0 µm | 0.20 | % | ISO 13468 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Circulation Dryer | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| Circulation Dryer | 3.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Smooth-Cast® ColorMatch® 326 | Smooth-On, Inc | PUR, Unspecified | Smooth-Cast® |
| APEX® RM 8911 | Teknor Apex Company | PVC, Rigid | APEX® |
| Durez® 32633 (Injection) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Epoxies, Ect. 20-3035 (Cat.140) | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| SQUARE® LIM2012-40A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |