| EVAL™F101B is an ethylene-vinyl alcohol (EVOH) product,. It is available in Europe. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 1.6 | g/10 min | ISO 1133 |
| 210°C/2.16 kg | 3.8 | g/10 min | ISO 1133 |
| Ethylene Content | 32.0 | mol% | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 34.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 | % | ISO 527-2 |
| Flexural Modulus | 3800 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability 1 | ISO 14663-2 | ||
| 20°C, 0% RH | 4.0E-3 | cm³·mm/m²/atm/24 hr | ISO 14663-2 |
| 20°C, 100% RH | 0.38 | cm³·mm/m²/atm/24 hr | ISO 14663-2 |
| 20°C, 35% RH | 6.0E-3 | cm³·mm/m²/atm/24 hr | ISO 14663-2 |
| 20°C, 65% RH | 8.0E-3 | cm³·mm/m²/atm/24 hr | ISO 14663-2 |
| 20°C, 85% RH | 0.030 | cm³·mm/m²/atm/24 hr | ISO 14663-2 |
| 20°C, 90% RH | 0.060 | cm³·mm/m²/atm/24 hr | ISO 14663-2 |
| Water Vapor Transmission Rate 2 | 1.6 | g·mm/m²/atm/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact Strength | 2.9 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 69.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 173 | °C | ISO 306 |
| Melting Temperature | 183 | °C | ISO 11357-3 |
| Peak Crystallization Temperature | 161 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Annex C |
| 2 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4902 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RABALON® SJ8300C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| Nipol® DN1201 | Zeon Chemicals L.P. | NBR | Nipol® |
| Cheng Yu FV30725 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| Tunhe PBS TH803S | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PBS | Tunhe PBS |