Braskem PE ML3400N
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GKUxV2_Braskem-PE-ML3400N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The resin ML3400N is a Linear Low Density Polyethylene developed for rotational molding. It presents good balance of processability, environmental stress cracking resistance and impact strength. Applications: This resin is indicated to produce rotomolded parts for general use applications, kayaks, toys, parts for the agricultural and automotive segments. Processing Conditions: Conditions comparable to polyethylene resins with similar melt index and density range. Recommended Oven Temperature Range: 220 to 350 °C. PIAT: 210 a 240°C Additives: Long term UV8 stabilization and antioxidants. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.935 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.5 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance 1 | ASTM D1693 | ||
| 50°C, 2.00mm, 10% Igepal, molded, F50 | 38.0 | hr | ASTM D1693 |
| 50°C, 2.00mm, 100% Igepal, molded, F50 | 400 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 17.0 | MPa | ASTM D638 |
| Fracture, molding | 25.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, molding | 17 | % | ASTM D638 |
| Fracture, molding | > 1000 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 530 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength | ARM | ||
| -40°C, 3.17mm, rotational molding | 46 | J | ARM |
| -40°C, 6.34mm, rotational molding | 120 | J | ARM |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, molded | 56.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, molded | 40.0 | °C | ASTM D648 |
| Peak Melting Temperature | 125 | °C | ASTM D3418 |
| Injection instructions |
|---|
| Recommended Rotational Molding Conditions: Oven Temperature Range: 220°C to 350°C |
| Note Message | |
|---|---|
| 1 . | 0.3mm notched-plaques |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1385 D | RTP Company | PPS | RTP |
| Mirakutoran® TPU E895 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Optema™ TC 220 ExCo | ExxonMobil Chemical | EMA | Optema™ |
| Hifax TRC 2044X BLACK | LyondellBasell Industries | PP, Unspecified | Hifax |
| Polyrocks EP8400S90V-1 | Polyrocks Chemical Co., Ltd | PE, Unspecified | Polyrocks |