Vydyne® ECO315J BK0707

Category: Nylon 66/6 , Polyamide 66/6 Copolymer
Manufacturer: Ascend Performance Materials Operations LLC
Trademark: Vydyne®
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: GKNgTk_VydyneECO315JBK0707.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Vydyne ECO315J BK0707 is a non-halogenated, unfilled, flame-retardant PA66/6 copolymer with excellent toughness and ductility. It is stabilized to provide heat stability up to 125°C for 1,000 hours in a dry environment. ECO315J BK0707 is also lubricated for machine feed and easy mold release and has an Underwriters Laboratories UL 94 flammability classification of V-0 at 0.4 mm (0.016") thick.
General Information
Additive
  • Lubricant
  • Flame retardancy
Features
  • Low density
  • Good cracking resistance
  • Good toughness
  • Lubrication
  • Good demoulding performance
  • Halogen-free
  • Extended tensile rate
  • ductility
  • Flame retardancy
Uses
  • Lighting Applications
  • Electrical/Electronic Applications
  • Electrical components
  • Electrical housing
  • Electrical appliances
  • Industrial application
  • Active hinge
  • Fasteners
  • Switch
  • Connector
  • Automotive Electronics
  • spool
  • Printed circuit board
UL File Number
  • E70062
Appearance
  • Black
Forms
  • Particle
Processing Method
  • Injection molding
PhysicalDryConditionedUnitTest Method
Density 1.16--g/cm³ISO 1183
Molding Shrinkage ISO 294-4
     Lateral flow : 23°C, 2.00mm 1.4--%ISO 294-4
     Traffic : 23°C, 2.00mm 1.2--%ISO 294-4
Water Absorption ISO 62
     23°C, 24 hr 0.80--%ISO 62
     Equilibrium, 23°C, 50% RH 2.3--%ISO 62
MechanicalDryConditionedUnitTest Method
Tensile Modulus (23°C)50003500MPaISO 527-2
Tensile Stress (Yield, 23°C)75.052.0MPaISO 527-2
Tensile Strain ISO 527-2
     Yield, 23°C 5.520%ISO 527-2
     Fracture, 23°C 2530%ISO 527-2
Flexural Modulus (23°C)32001560MPaISO 178
Flexural Strength (23°C)92.045.0MPaISO 178
Poisson's Ratio 0.40--ISO 527-2
ImpactDryConditionedUnitTest Method
Charpy Notched Impact Strength ISO 179/1eA
     -30°C 5.4--kJ/m²ISO 179/1eA
     23°C 5.4--kJ/m²ISO 179/1eA
Charpy Unnotched Impact Strength ISO 179/1eU
     -30°C No Break--ISO 179/1eU
     23°C No Break--ISO 179/1eU
Notched Izod Impact (23°C)6.0--kJ/m²ISO 180
ThermalDryConditionedUnitTest Method
Heat Deflection Temperature
     0.45 MPa, not annealed 225--°CISO 75-2/B
     1.8 MPa, not annealed 65.0--°CISO 75-2/A
Melting Temperature 244--°CISO 11357-3
Linear thermal expansion coefficient ISO 11359-2
     Flow : 23 to 55°C, 2.00mm 1.1E-4--cm/cm/°CISO 11359-2
     Lateral : 23 to 55°C, 2.00mm 1.1E-4--cm/cm/°CISO 11359-2
RTI Elec UL 746
     0.40 mm 130--°CUL 746
     0.75 mm 130--°CUL 746
     1.5 mm 130--°CUL 746
     3.0 mm 130--°CUL 746
RTI Imp UL 746
     0.40 mm 65.0--°CUL 746
     0.75 mm 65.0--°CUL 746
     1.5 mm 85.0--°CUL 746
     3.0 mm 85.0--°CUL 746
RTI UL 746
     0.40 mm 100--°CUL 746
     0.75 mm 100--°CUL 746
     1.5 mm 100--°CUL 746
     3.0 mm 110--°CUL 746
ElectricalDryConditionedUnitTest Method
Volume Resistivity (0.750 mm)1.0E+11--ohms·cmIEC 60093
Dielectric Strength (1.00 mm)13--kV/mmIEC 60243
Arc Resistance (3.00 mm)PLC 5--ASTM D495
Comparative Tracking Index (3.00 mm)600--VIEC 60112
High Amp Arc Ignition (HAI) UL 746
     0.40 mm PLC 0--UL 746
     0.75 mm PLC 0--UL 746
     1.5 mm PLC 0--UL 746
     3.0 mm PLC 0--UL 746
High Voltage Arc Tracking Rate (HVTR) PLC 1--UL 746
Hot-wire Ignition (HWI) UL 746
     0.40 mm PLC 4--UL 746
     0.75 mm PLC 4--UL 746
     1.5 mm PLC 4--UL 746
     3.0 mm PLC 3--UL 746
FlammabilityDryConditionedUnitTest Method
Flame Rating UL 94
     0.40 mm V-0--UL 94
     0.75 mm V-0--UL 94
     1.5 mm V-0--UL 94
     3.0 mm V-0--UL 94
Glow Wire Flammability Index IEC 60695-2-12
     0.40 mm 960--°CIEC 60695-2-12
     0.75 mm 960--°CIEC 60695-2-12
     1.5 mm 960--°CIEC 60695-2-12
     3.0 mm 960--°CIEC 60695-2-12
Glow Wire Ignition Temperature IEC 60695-2-13
     0.40 mm 875--°CIEC 60695-2-13
     0.75 mm 875--°CIEC 60695-2-13
     1.5 mm 775--°CIEC 60695-2-13
     3.0 mm 725--°CIEC 60695-2-13
Oxygen Index 29--%ISO 4589-2
InjectionDryUnit
Drying Temperature 80°C
Drying Time 4.0hr
Suggested Max Regrind 50%
Rear Temperature 240 - 270°C
Middle Temperature 240 - 270°C
Front Temperature 240 - 270°C
Nozzle Temperature 240 - 270°C
Processing (Melt) Temp 250 - 270°C
Mold Temperature 65 - 95°C
Resin Grade Manufacturer Category Trademark
PONACOM ABS 7315 Ponachem Compound GmbH ABS PONACOM ABS
WONDERLITE® PC-110U CHI MEI CORPORATION PC WONDERLITE®
Alpha PVC GW 2052 SPEC NAT LCF AlphaGary PVC, Unspecified Alpha PVC
Grilamid® XE 4071 nat EMS-GRIVORY Nylon 612 Grilamid®
Perlast® G90A Precision Polymer Engineering Ltd. Perfluoroelastomer Perlast®