NORYL™ FE1520PW resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GKNf6q_NORYLFE1520PWresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Noryl* FE1520PW resin is a blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20% glass reinforcement. The resin is suitable for injection molding. Noryl FE1520PW resin has been developed for fluid engineering applications that require improved hydrolytic stability. Noryl FE520PW resin has been certified for potable water applications up to 85C in Europe and North America in limited colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/10.0 kg) | 22.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.20 - 0.40 | % | Internal method |
| Transverse flow : 3.20mm | 0.30 - 0.60 | % | Internal method |
| Water Absorption | |||
| Saturated, 23°C | 0.20 | % | ISO 62 |
| Balance, 50% RH | 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 220 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7110 | MPa | ASTM D638 |
| -- | 7180 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 119 | MPa | ASTM D638 |
| Fracture | 119 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 2.6 | % | ASTM D638 |
| Fracture | 2.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 6970 | MPa | ASTM D790 |
| -- 5 | 6040 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 165 | MPa | ISO 178 |
| Fracture, 50.0mm span 6 | 175 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 65.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 7 | 5.0 | kJ/m² | ISO 179/1eA |
| -30°C | 27 | kJ/m² | ISO 179/2C |
| 23°C | 6.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 8(23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| -30°C | 45 | J/m | ASTM D256 |
| 23°C | 65 | J/m | ASTM D256 |
| -30°C 9 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 400 | J/m | ASTM D4812 |
| 23°C | 400 | J/m | ASTM D4812 |
| -30°C 11 | 23 | kJ/m² | ISO 180/1U |
| 23°C 12 | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 100 mm span 13 | 132 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.20mm | 135 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 14 | 139 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A50 |
| -- | 144 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 250 - 270 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Nozzle Temperature | 280 - 300 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 sp=62mm |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 120*10*4 mm |
| 14 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Clariant Nylon 6/6 PA-111G33 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| CompaDur® 125 GF 30 black (047) | DimeLika Plast GmbH | PBT+PET | CompaDur® |
| G-PAEK™ 1100G | Gharda Chemicals Ltd. | PEK | G-PAEK™ |
| Elastron® G G500.A80.N.PA | Elastron USA, Inc. | SEBS | Elastron® G |
| POLYelast TPE EDS80 D35 | Polykemi AB | PP+EPDM | POLYelast |