TECACOMP® PPS TC black 4084
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GKCDWv_TECACOMPPPSTCblack4084.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (316°C/5.0 kg) | 50 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (316°C/5.0 kg) | 30.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.63 | % | ISO 294-4 |
| Flow | 0.58 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/50 |
| Tensile Stress | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 0.50 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 6.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 90.0 | °C | DIN 53765 |
| Melting Temperature | 280 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 1.8E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 100 to 200°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 100 to 200°C | 5.7E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 1 | 2.0 | W/m/K | DIN EN 821 |
| -- 2 | 7.3 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| long term | 230 | °C | |
| short term | 260 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electrical Conductivity | 5.30 | S/m | ISO 3915 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.4E+5 | ohms | DIN EN 61340 |
| Volume Resistivity | 19 | ohms·cm | ISO 3915 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | V-0 | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 - 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Processing (Melt) Temp | 300 - 370 | °C | |
| Mold Temperature | 140 - 200 | °C |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 218 BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Wellamid® GF30-60 XE-NBK1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| ABSCOM® CP1350 | Polymer Compounders Limited | ABS | ABSCOM® |
| Jiangsu Sinarise EX8534X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| TORZEN® G3000HSL BK20 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |