LNP™ LUBRICOMP™ HFG25Z compound
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GK3le8_LNP-LUBRICOMP-HFG25Z-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* HFG25Z is a compound based on Nylon 11 resin containing 25% Glass Fiber, 10% Graphite. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound HFL-4325 Product reorder name: HFG25Z |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.40 to 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.80 to 1.0 | % | ASTM D955 |
| Across Flow : 24 hr | 0.93 | % | ISO 294-4 |
| Flow : 24 hr | 0.47 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11000 | MPa | ASTM D638 |
| -- | 6830 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 152 | MPa | ASTM D638 |
| Yield | 76.0 | MPa | ISO 527-2 |
| Break | 152 | MPa | ASTM D638 |
| Break | 76.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.7 | % | ASTM D638 |
| Yield | 2.3 | % | ISO 527-2 |
| Break | 2.7 | % | ASTM D638 |
| Break | 2.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5520 | MPa | ASTM D790 |
| -- | 18200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 96.5 | MPa | ASTM D790 |
| -- | 352 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.42 | ||
| vs. Itself - Static | 0.46 | ||
| Wear Factor - Washer | 58.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 2 | 7.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 450 | J/m | ASTM D4812 |
| 23°C 3 | 29 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 15.1 | J | ASTM D3763 |
| -- | 3.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 182 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 182 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 171 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 166 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 9.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 3.4E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 199 to 210 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 227 to 260 | °C | |
| Mold Temperature | 43.3 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makropol® PC A3 G30 HUV NTL0001 PC308 | Petropol Industry and Trade of Polymers LTDA | PC | Makropol® PC |
| Estane® ETE 50DT3 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| HiFill® PA11 GB30 HS | Techmer Engineered Solutions | Nylon 11 | HiFill® |
| PERLER® O07N2000A10 | A.D. Compound S.p.A. | PP Copolymer | PERLER® |
| Sylvin 8983-65 White 1196 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |